China (Mainland)
- Product Details
Keywords
- POLYETHER POLYOL
- PPG and POP
- TDI and MDI
Quick Details
- ProName: polyurethane foam PPG and POP
- CasNo: 9003-11-6
- Molecular Formula: HO.(C2H4O)m.(C3H6O)n.H
- Appearance: colorless or pale yellow liquid
- Application: PPG is used as solubilizing agent, ant...
- ProductionCapacity: Metric Ton/Day
- Purity: ≥99%
- LimitNum: 5 Metric Ton
Superiority
It has good quality and competitive price;
Details
| Trademark | Hydroxyl value | Acid value | Water content | pH | Unsaturated value | Viscosity | K+ | Colourity | Application | Feature | |
| mgKOH/g | mgKOH/g | % | mol/kg | mPa·s/25℃ | mg/kg | APHA | |||||
| Polyether Ployols For Elastomer, Coating, Adhesive | 204 | 265-295 | ≤0.05 | ≤0.05 | 5-7 | - | 60-80 | ≤5 | ≤50 | This is a low unsaturated polypropylene oxide ether diol, with a molecular weight of 400-8000. As the basis component for the soft segment structure of polyurethane, it can be used for a variety of polyurethane waterproof products. | This series products are mainly used for CASE series products, with a molecular weight range from 700 to 12000. For application, as the molecular weight of the polyol increases, the elongation at break gradually increases while the tensile strength and hardness decreases. Users may choose polyether polyols of different molecular weight according to their final product’s request. They can also arrange 3050, 330NG or 3600 in groups to increase the product’s tensile strength |
| 210 | 107-117 | ≤0.05 | ≤0.02 | 5-8 | - | 120-180 | - | - | |||
| 220 | 54.5-57.5 | ≤0.05 | ≤0.02 | 5-8 | ≤0.01 | 270-370 | - | - | |||
| 230 | 35-39 | ≤0.05 | ≤0.02 | 5-8 | ≤0.01 | 500-600 | - | - | |||
| 240 | 26.5-29.5 | ≤0.05 | ≤0.02 | 5-8 | ≤0.01 | 800-1000 | - | - | |||
| 3050DF | 54.5-57.5 | ≤0.05 | ≤0.05 | 5-7 | ≤0.01 | 400-700 | - | - | This is a low unsaturated polypropylene oxide ether triol, with a molecular weight of 3000. It can be used for a variety of pavement polyurethane products, effectively improving the tensile strength of the polyurethane products. | It can not be used to prepare flexible polyurethane foam, as it may cause sponge heartburn. | |
| 3600 | 26.5-29.5 | ≤0.06 | ≤0.05 | 5-7 | ≤0.08 | 1000-1600 | ≤5 | ≤50 | With a functionality of 3 and molecular weight of 6000, this high-activity polyether polyol can be used to produce pavement polyurethane materials, which have a higher tensile strength and resilience | ||
| 330N(G) | 32.5-35.5 | ≤0.05 | ≤0.05 | 5-7 | ≤0.07 | 800-1000 | ≤3 | ≤50 | With a functionality of 3 and molecular weight of 5000, this high-activity polyether polyol can be used for CASE series products, which have a higher tensile strength and resilience. | ||
| Polyether ployols for Flexible Foams | 5631D | 54.5-57.5 | ≤0.05 | ≤0.05 | 5-7 | ≤0.01 | 400-700 | - | - | Low, middle and high density soft block Polyurethane foam for packing and cushion materials. | 1. Higher activity than MN-3050D. When produce low density foam ,it less prone to collapse bubbles, cracks and other abnormal defects. 2. with low unsaturated value and average functionality over 2.9,the foam made by it has higher tensile strength and indentation hardness, and less permanent deformation than traditional soft foam. 3. Has antioxidant of BHT. |
| 5631ED | 54.5-57.5 | ≤0.05 | ≤0.05 | 5-7 | ≤0.01 | 400-700 | - | - | Without BHT and with strong anti-yellow capability | ||
| 3050 | 54.5-57.5 | ≤0.05 | ≤0.05 | 5-7 | ≤0.01 | 400-700 | - | - | Middle and high density soft block polyurethane foams for packing and cushion materials. | 1. less activity than 5631D and not fit for low density form. When be used in wide middle and high density foam, it is easier for users to adjust the formula. 2. with low unsaturated value and average functionality over 2.9,the foam made by it has higher tensile strength and indentation hardness, and less permanent deformation than traditional soft foam. 3. Has antioxidant of BHT. | |
| Highly Active Polyether | 330N（G） | 32.5-35.5 | ≤0.05 | ≤0.05 | 5-7 | ≤0.07 | 800-1000 | ≤3 | ≤50 | High activity polyether . Mixed with polymer polyol grafted polyether together. Used in producing high resilience, cold cured foam for cushions of automobiles, motorcycles, bicycles and steering wheels. | With a functionality of 3, molecular weight of 5000, and low ordor, this kind of high-activity polyether polyol can be used to produce high resilience slabstock foam, effectively enhancing the resilience of foams. It can be also used to produce molded foam, which has a higher activity, shorter stripping time. It is particularly suitable for the preparation of a variety of automobile interior materials. |
| 330N(Y) | 32.5-35.5 | ≤0.08 | ≤0.05 | 5-7 | ≤0.07 | 800-1000 | ≤3 | ≤50 | Comparing with 330N(G), this product can minimize the odor. | ||
| 3600 | 26.5-29.5 | ≤0.06 | ≤0.05 | 5-7 | ≤0.08 | 1000-1600 | ≤5 | ≤50 | Mixed with polymer polyol grafted polyether together. Used in producing high resilience, cold cured foam for cushions of automobiles, motorcycles, bicycles and steering wheels. It can also be used to produce automobile sealant. | With a functionality of 3 and molecular weight of 6000, this high-activity polyether polyol can be used to produce high resilience slabstock foam, effectively enhancing the resilience of foams. It can be also used to produce molded foam, which has a higher activity, shorter stripping time. Comparing with 330NY, 3600 can be used to prepare more resilient foam with less hardness. This product can also be used for CASE series, which can effectively improve its tensile strength and resilience. | |
| Ployether Polyols For Rigid Foams | 4110 | 430-470 | ≤0.20 | ≤0.20 | 9-12 | - | 3000-6000 | ≤8 | ≤8 | Used in refrigerators, freezers, cold storage, solar energy, painting, sheet, pipe thermal insulation material. | Classic, Broad-spectrum sucrose rigid PPG which is the base material of rigid foam, and fits various foaming system with good liquidity and moderate activity |
| 8345 | 440-460 | ≤0.30 | ≤0.10 | 4-6 | - | 6000-10000 | ≤8 | ≤8 | Used in refrigerators, freezers, cold storage and other Polyurethane heat preservation, cold insulation material | With moderate Functionality and viscosity,it is fit for various foaming system solely or with other rigid PPG. Balance between foam mobility and dimensional stability is favorable for Polyurethane heat preservation boards. | |